Test procedures under scrutiny

Co-author Tobias Neuwirth adjusts the setup for the neutron grating interferomet

Co-author Tobias Neuwirth adjusts the setup for the neutron grating interferometry at the ANTARES instrument of the research neutron source Heinz Maier-Leibnitz (FRM II) at the Technical University of Munich. Image: B. Ludewig / TUM

Comparatively, neutrons detect most defects in 3D printed components

In the manufacture of turbines conventional processes often reach their limits. Therefore, additive manufacturing is increasingly used to produce complex, curved components with intricate structures. A research team from the Technical University of Munich (TUM) has now examined common methods used to locate defects inside components. In their investigation neutron grating interferometry, performed at the Heinz Maier-Leibnitz research neutron source (FRM II), achieved the best defect detection.

Laser beam melting is a common 3D printing process for turbine blades with internal cooling channels. During this process, a laser melts a thin layer of metal powder in predefined areas. Layer by layer, the component forms in a bed of powder. Similar to an archeological excavation, the component is then exposed and the remaining powder can be reused for the next printing process.

However, process instabilities can lead to defects and reduce the strength of the component. Typical defects are pores and cracks. Even partial or total separation of individual layers can occur.

Defects in safety-relevant components, such as turbine blades, can lead to serious consequences. "We therefore need to examine critical components after the manufacturing process and of course do so non-destructively," explains Cara Kolb from the Institute for Machine Tools and Industrial Management at TUM.

For their experiments, the researchers produced test specimens with defects of different size and depth and then attempted their detection using non-destructive testing methods. This involved active infrared thermography (aIRT), ultrasonic testing (UT), X-ray computed tomography (CT) and neutron grating interferometry (nGI).

At the research neutron source doctoral candidate Tobias Neuwirth conducted the experiments at the ANTARES instrument. "We investigate components using neutron grating interferometry, observing the scattering and absorption of neutrons in a spatially resolved manner. Changes in these properties give us information about the type and size of the defects," he explains.

Each of the methods tested has both potential and challenges. Neutron grating interferometry is complex and more expensive than the other test methods investigated, but of all the methods, it detected the most and the smallest defects.

"Neutrons can penetrate deep into the material and resolve the internal component structure with high resolution. They are particularly suited to nickel-based alloys, which are enormously important for the additive manufacturing of structural components in aerospace," concludes Cara Kolb.

Research into testing procedures that non-destructively assure the quality of 3D-printed components is very important: Such procedures reveal the likelihood of a component failure during operation. They are also ever more important as additive manufacturing in aircraft and cars, for example, increases.

C. G. Kolb, K. Zier, J.-C. Grager, A. Bachmann, T. Neuwirth, S. Schmid, M. Haag, M. Axtner, F. Bayerlein, C. U. Grosse, M. F. Zaeh An investigation on the suitability of modern nondestructive testing methods for the inspection of specimens manufactured by laser powder bed fusion SN Appl. Sci., 3, 713 (2021) - DOI: https://doi.org/10.1007/s42452-021-04685-3